API RP 571 describes under Caustic Corrosion:

“One of the significant contributing factors is caustic accumulation in low-flow or stagnant areas, especially in heat-traced lines or around steam injection points.”

“Localized heating can concentrate caustic solutions, promoting corrosion even in carbon or stainless steels.”

Thus, option C (heat-traced equipment) is the correct and technically accurate choice.

Comprehensive and Detailed Explanation From Exact Extract:

Per API RP 571, sulfidation corrosion rates are significantly accelerated by the presence of hydrogen. Hydrogen promotes:

Breakdown of protective sulfide scales

Increased diffusion of sulfur into the metal

Higher metal loss rates

This phenomenon is often referred to as hydrogen-assisted sulfidation and is commonly observed in refinery process units.

Moisture is more closely associated with oxidation mechanisms rather than high-temperature sulfidation.

Referenced Documents (Study Basis):

API RP 571 – Section on Sulfidation and High-Temperature Corrosion

API RP 751 (referenced in RP 571) lists materials appropriate for HF acid alkylation service. It specifies:

“Chrome-moly steels such as ASTM A-193 B5 (5% Cr) bolts are preferred for their resistance to HF acid-induced cracking.”

“Standard low alloy steels (e.g., B7) are not considered adequately resistant.”

(Reference: API RP 571 summary & API RP 751, Section 5.6.3 – Bolting Materials)

Therefore, the correct and industry-approved answer is option A.

API RP 571 under Oxidation:

“Carbon steels and low alloy steels, such as 9 Cr, have poor oxidation resistance at temperatures above 1000°F (540°C), rapidly losing thickness.”

“Stainless steels with higher Cr and Ni content (like 310) have superior oxidation resistance.”

Thus, 9 Cr steel will corrode fastest at 1350°F, making option D correct.