API RP 571 under Cooling Water Corrosion and Scaling:

“Cooling water scaling tends to occur more rapidly as water temperature increases. To minimize scaling, inlet temperatures to exchangers should be kept below 140°F (60°C) where possible.”

“Above this temperature, calcium carbonate and other salts tend to precipitate more readily.”

Thus, option A is correct.

According to API RP 571, under Oxidation:

“Austenitic stainless steels (300 Series) are generally used for oxidation resistance up to about 1500°F (815°C). At higher temperatures, scaling and loss of protective chromium oxide layers increase.”

“Above these temperatures, specialized high-temperature alloys may be required.”

(Reference: API RP 571, Section 5.1.1 – Oxidation)

Therefore, option C is the correct answer.

According to API RP 571, under Naphthenic Acid Corrosion (NAC):

“The most severe corrosion is typically found in areas of high velocity and turbulence, such as at pump around nozzles, transfer lines, elbows, reducers, and orifices.”

“NAC is characterized by uniform thinning and can accelerate significantly where flow-induced erosion is present.”

(Reference: API RP 571, Section 4.3.4.1 – Naphthenic Acid Corrosion)

This clearly establishes that high velocity and turbulence increase NAC severity, making option D correct.

Comprehensive and Detailed Explanation From Exact Extract:

Carbolic acid corrosion (phenol corrosion) is described in API RP 571 as a process-specific corrosion mechanism that may not produce distinct or easily detectable wall-loss patterns using conventional NDE methods.

API RP 571 emphasizes that confirmation of carbolic acid corrosion often requires:

Chemical identification of corrosion products

Metallurgical examination

Verification of acid presence and metal interaction

A boat sample (also known as a coupon or scoop sample) removed from the affected area and analyzed in a laboratory allows:

Identification of corrosion morphology

Chemical analysis of deposits

Confirmation of phenol-related attack

Why the other options are incorrect:

UT and RT detect wall loss but cannot identify the corrosion mechanism.

Acoustic emission detects active cracking, not specific corrosion chemistry.

Angle beam UT is for crack detection, not corrosion identification.

Therefore, laboratory analysis of a removed sample is the most useful method.

Referenced Documents (Study Basis):

API RP 571 – Section on Organic Acid Corrosion (Phenols)

API Corrosion Failure Analysis Study Guide

======================